ZR6005 (light yellow)

Chuyên cho ô tô

Cơ tính cao, bền, ít biến dạng, chịu nhiệt tốt


ZR680 ( Accurate & White )




THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS
( LIQUID STATE )

Appearance: White liquid

Density: 1.10 g/cm³@25℃

Viscosity: 450 CPS@25℃

Dp: ≥0.16 mm

Ec: 8.5 mJ/cm²

MOLDING PERFORMANCE A

@355nm point laser@330mW power@5.0m/s scanning@No UV post-cure



– Bending Modulus:
1500~1700 MPa

– Bending Strength: 55~60 MPa

– Notched Impact Strength: 60~68 J/m

– 1.2mm Bend Angle 140~170°
MOLDING PERFORMANCE B

@90min UV post-cure



– Bending Modulus:
2688~2790 MPa

– Bending Strength:
66~73 MPa

– Notched Impact Strength:
60~68 J/m

– Hardness :88

– Elongation at break: 10~15%

– HDT ( Heat deflection temperature ) 52 ℃

– Tg Glass transition temperature: 62 ℃

– CTE Coefficient of thermal expansion: 93*E-6

ZR710 ( Tough & White )



THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS
( LIQUID STATE )

Appearance: White liquid

Density: 1.10 g/cm³@25℃

Viscosity: 400 CPS@25℃

Dp: ≥0.16 mm

Ec: 7.9 mJ/cm²

MOLDING PERFORMANCE A

@355nm point laser
@330mW power
@5.0m/s scanning
@No UV post-cure



– Bending Modulus:
2000~2300 MPa

– Bending Strength: 75~85 MPa

– Notched Impact Strength: 35~45 J/m

– 1.2mm Bend Angle ≥170~180°
MOLDING PERFORMANCE B

@90min UV post-cure



– Bending Modulus:
2813~3520 MPa

– Bending Strength:
83~90 MPa

– Notched Impact Strength:
42~50 J/m

– Hardness :87~92

– Elongation at break: 13~20%

– HDT ( Heat deflection temperature ) 52 ℃

– Tg Glass transition temperature: 62 ℃

– CTE Coefficient of thermal expansion: 93*E-6

ZR820 ( High Transparency )



THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS
( LIQUID STATE )

Appearance: Transparent liquid Pale Purple

Density: 1.10 g/cm³@25℃

Viscosity: 190 CPS@25℃

Dp: ≥0.18 mm

Ec: 6.9 mJ/cm²

MOLDING PERFORMANCE A

@355nm point laser
@330mW power
@5.0m/s scanning
@No UV post-cure



– Appearance: High Transparency

-Transmittance: 85%(MAX)

– Bending Modulus:
1500~1700 MPa

– Bending Strength: 45~55 MPa

– Notched Impact Strength: 25~35 J/m

– 1.2mm Bend Angle:140~170°
MOLDING PERFORMANCE B

@90min UV post-cure



– Bending Modulus:
1890~2340 MPa

– Bending Strength:
55~62 MPa

– Notched Impact Strength:
40~55 J/m

– Hardness :79

– Elongation at break: 10~15%

– HDT ( Heat deflection temperature ) 52 ℃

– Tg Glass transition temperature: 62 ℃

– CTE Coefficient of thermal expansion: 93*E-6

Real ABS ( ABS Like )




THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS
( LIQUID STATE )

Appearance: Bright yellow liquid

Density: 1.10 g/cm³@25℃

Viscosity: 400 CPS@25℃

Dp: ≥0.16 mm

Ec: 7.9 mJ/cm²

MOLDING PERFORMANCE A

@355nm point laser
@330mW power
@5.0m/s scanning
@No UV post-cure


– Bending Modulus: 2000~2300 MPa

– Bending Strength: 45~55 MPa

– Notched Impact Strength: 35~45 J/m

– 1.2mm Bend Angle:≥170~180°
MOLDING PERFORMANCE B

@90min UV post-cure



– Bending Modulus:
2813~3520 MPa

– Bending Strength:
83~90 MPa

– Notched Impact Strength:
42~50 J/m

– Hardness :87~92

– Elongation at break: 13~20%

– HDT ( Heat deflection temperature ) 52 ℃

– Tg Glass transition temperature: 62 ℃

– CTE Coefficient of thermal expansion: 93*E-6

Red Wood ( Tooling Board Like )



THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS
( LIQUID STATE )

Appearance: Epoxy Tooling Board Like (Pink) liquid

Density: 1.10 g/cm³@25℃

Viscosity: 400 CPS@25℃

Dp: ≥0.16 mm

Ec: 7.9 mJ/cm²

MOLDING PERFORMANCE A

@355nm point laser
@330mW power
@5.0m/s scanning
@No UV post-cure


– Bending Modulus:
2000~2300 MPa

– Bending Strength: 75~85 MPa

– Notched Impact Strength: 35~45 J/m

– 1.2mm Bend Angle:≥170~180°
MOLDING PERFORMANCE B

@90min UV post-cure



– Bending Modulus:
2813~3520 MPa

– Bending Strength:
83~90 MPa

– Notched Impact Strength:
42~50 J/m

– Hardness :87~92

– Elongation at break: 13~20%

– HDT ( Heat deflection temperature ) 52 ℃

– Tg Glass transition temperature: 62 ℃

– CTE Coefficient of thermal expansion: 93*E-6

.
.
.
.