Công Nghệ In 3D SLS Cao Cấp Công Nghiệp

ZRPA12 ( PA12 Nylon Powder )


THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS

Grain Size50~55μm

ShapeSpherical

Apparent density≥0.40 g/cm³

THERMAL PROPERTY


Melting Point182~185℃(10℃/min)
Melting Enthalpy≥90 J/g
HDT83.8℃@1.8MPa /

146.1℃@0.45MPa

MOLDING PERFORMANCE


Density0.97 g/cm³
Tensile Modulus1600 MPa
Tensile Strength43 MPa
ElongatioFFn at break≥15 %
Un-notched Impact Strength20.7 KJ/m²
Notched Impact Strength3.8 KJ/m²
Bending Modulus1432 MPa
Bending Strength57 MPa

GF100 ( Glass Fiber Composite Nylon Powder )


THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS
Apparent density: ≥0.66 g/cm³


THERMAL PROPERTY


Melting Point183℃(10℃/min)
HDT89℃@1.8MPa / 163℃@0.45MPa


MOLDING PERFORMANCE


Density1.24 g/cm³
Tensile Modulus3498 MPa
Tensile Strength43 MPa
Elongation at break5 %
Un-notched Impact Strength19.26 KJ/m²
Notched Impact Strength4.11 KJ/m²
Bending Modulus2413 MPa
Bending Strength67 MPa

MF100 ( Mineral Fiber Composite Nylon Powder )


THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS
FFApparent density: ≥0.53 g/cm³

THERMAL PROPERTY


Melting Point180℃(10℃/min)
HDT125℃@1.8MPa / 170℃@0.45MPa


MOLDING PERFORMANCE


Density1.18 g/cm³
Tensile Modulus6128 MPa
Tensile Strength50 MPa
Elongation at break4.6 %
Un-notched Impact Strength20.75 KJ/m²
Notched Impact Strength5.58 KJ/m²
Bending Modulus4630 MPa
Bending Strength74 MPa

ZRTPU ( Thermoplastic Polyurethanes Powder )


THÔNG SỐ KỸ THUẬT
PHYSICAL CHARACTERISTICS
Grain Size60μm
ShapeSpherical
Apparent density0.47 g/cm³


THERMAL PROPERTY


Melting Point165℃
HDTHeat deflection temperature-25℃



MOLDING PERFORMANCE


Density1.15 g/cm³
Tensile Modulus61 MPa
Tensile Strength21 MPa
Elongation at break310 %
Tear strength101 N/mm
Bending Modulus74 MPa
Bending Strength3.3 MPa


Product Specifications

.
.
.
.